Forged stainless steel HR key pin shackle and bar.
Half turn opening captive pin shackle with removable bar.
‘HR’ stands for High Resistance.Shackle forged in HR 17.4 Ph stainless steel can be up to 60% more resistant than a shackle made from 316L stainless steel.
Hot dropped forged from a single piece of stainless steel, adding strength and consistency of manufacture for total security and reliability. The technical characteristics of every Shackle is closely controlled and tested before, during and after the manufacturing process.
Version 81432 (Materials 316 stainless steel grade)
- Working load (kg)400
- Breaking load (kg)1200
- Weight (g)31
- A (mm)37
- B (mm)13
- C (mm)5
- D (mm)11
- D diameter (mm)5
- E (mm)4
- F (mm)49
- G (mm)31
- L (mm)12
Version 91432 (Materials HR 17.4 PH stainless steel grade)
- Working load (kg)480
- Breaking load (kg)1500
- Weight (g)31
- A (mm)37
- B (mm)13
- C (mm)5
- D (mm)11
- E (mm)4
- F (mm)49
- G (mm)31
- L (mm)12
Version 81433 (Materials 316 stainless steel grade)
- Working load (kg)520
- Breaking load (kg)1700
- Weight (g)52
- A (mm)45
- B (mm)16
- C (mm)6
- D (mm)13
- D diameter (mm)6
- E (mm)4
- F (mm)60
- G (mm)37
- L (mm)15
Version 91433 (Materials HR 17.4 PH stainless steel grade)
- Working load (kg)600
- Breaking load (kg)2200
- Weight (g)53
- A (mm)45
- B (mm)16
- C (mm)6
- D (mm)13
- E (mm)4
- F (mm)60
- G (mm)37
- L (mm)15
Version 81434 ((Materials 316 stainless steel grade)
- Working load (kg)800
- Breaking load (kg)2500
- Weight (g)123
- A (mm)59
- B (mm)21
- C (mm)8
- D (mm)17
- D diameter (mm)8
- E (mm)6
- F (mm)79
- G (mm)49
- L (mm)20
Version 91434 (Materials HR 17.4 PH stainless steel grade)
- Working load (kg)960
- Breaking load (kg)3500
- Weight (g)123
- A (mm)59
- B (mm)21
- C (mm)8
- D (mm)17
- E (mm)6
- F (mm)79
- G (mm)48
- L (mm)20